Adjusting the texture and nitrogen content of ordered mesoporous ...
2013-08-03 09:37:44    Editor:ciclab    View:[]

N. N. Liu, L. W. Yin, C. X. Wang, L. Y. Zhang, N. Lun, D. Xiang, Y. X. Qi and R. Gao,Adjusting the texture and nitrogen content of ordered mesoporous nitrogen-doped carbon materials prepared using SBA-15 silica as a template,Carbon,2010,48(12), 3579-3591.

Mesoporous nitrogen-doped carbon (N-MC) with highly ordered two dimensional hexagonal structures has been synthesized using diaminobenzene (DAB) as carbon and nitrogen sources, ammonium peroxydisulfate (APDS) as an oxidant, and SBA-15 as a hard template. The effect of synthesis temperatures and precursors on the textures and nitrogen content of the N-MC is investigated. By adjusting the synthesis temperatures in a range of 70-100 degrees C, the pore diameter of the N-MC materials can be tuned from 3.43 to 4.15 nm, while the specific surface area of the N-MC with a nitrogen content of 26.5 wt.%, can be tuned from 281.8 to 535.2 m(2)/g. The C/N molar ratio of the N-MC can be tuned in a range of 3.25-3.65 by adjusting the mole ratio of DAB/APDS precursors at a synthesis temperature of 80 C, while the pore diameter of the N-MC be tuned in a range of 4.12-3.66 rim. With the nitrogen doping content increasing, the lattice constant of N-MC materials decreases. Investigation indicates that well ordered N-MC materials with large specific surface area, high total pore volume and high nitrogen content can be fabricated under a synthesis temperature of 80 C and a molar ratio of 1.5 for DAB/APDS precursors.

Next:One-Pot Synthesis of PtRu Nanoparticle Decorated Ordered Mesoporous Carbons with

[CLOSE]

Copyright ? 2012-2015 Key Laboratory of Collid and Interface Chemistry, Ministry of Education(Shandong University). All Rights Reserved.
Add: NO.27 Shandanan Road, Jinan, China Tel / Fax: 86-531-88364750 Email: ciclab@sdu.edu.cn